FILM OF A VINYL ALCOHOL COPOLYMER, SOLUBLE IN COLD WATER, THICKNESS OF 34 UM OR MORE AND NOT EXCEEDING 90 UM, TENSILE STRENGTH AT BREAK OF 32.8 (+/- 12.1) MPa, ELONGATION AT BREAK OF 675 (+/- 225) %.
FILM OF A VINYL ALCOHOL COPOLYMER, SOLUBLE IN COLD WATER, THICKNESS OF 34 UM OR MORE AND NOT EXCEEDING 90 UM, TENSILE STRENGTH AT BREAK OF 32.8 (+/- 12.1) MPa, ELONGATION AT BREAK OF 675 (+/- 225) %.
FILM OF A VINYL ALCOHOL COPOLYMER, SOLUBLE IN COLD WATER, THICKNESS OF 34 UM OR MORE AND NOT EXCEEDING 90 UM, TENSILE STRENGTH AT BREAK OF 32.8 (+/- 12.1) MPa, ELONGATION AT BREAK OF 675 (+/- 225) %.
Justification du classement
CLASSIFICATION IS DETERMINED BY GENERAL RULES 1 & 6 TOGETHER WITH THE TEXT TO CN CODES 3920, 392099 AND 39209959.