1C005

"Superconductive""composite" conductors containing one or more niobium-titanium ‘filaments’, having all of the following: 1. Embedded in a "matrix" other than a copper or copper-based mixed "matrix"; and 2. Having a cross-section area less than 0,28 × 10-4 mm^2 (6 μm in diameter for circular ‘filaments’);

"Superconductive""composite" conductors consisting of one or more "superconductive"‘filaments’ other than niobium-titanium, having all of the following: 1. A "critical temperature" at zero magnetic induction exceeding 9,85 K (– 263,31 °C); and 2. Remaining in the "superconductive" state at a temperature of 4,2 K (– 268,96 °C) when exposed to a magnetic field oriented in any direction perpendicular to the longitudinal axis of conductor and corresponding to a magnetic induction of 12 T with critical current density exceeding 1 750 A/mm^2 on overall cross-section of the conductor;

"Superconductive""composite" conductors consisting of one or more "superconductive"‘filaments’ which remain "superconductive" above 115 K (– 158,16 °C).